Coated Surfacing Electrode Stellite 6 Aws Ecocr-a Stellite 6 Welding Rods

• Type: Cobalt Based Alloy Welding Electrode
• Material: Cobalt Based
• Diameter: 3.2mm
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: Stellite 6
• Length: 350mm
• Welding Core Type: Alloy
• Electrode Coating Type: Alkaline
• Slag Characteristic: Alkaline
• Function: Hardfacing Electrode
• Welding Power: DC
• Delivery Time: 15 Days
• MOQ: 20kg
• Package: 5kg/Box
• Product Length: 350mm
• Transport Package: 5kg/Box
• Specification: 2.7mm, 3.2mm, 4.0mm
• Trademark: Xunzhuo
• Origin: China
• HS Code: 8311100000
• Production Capacity: 5000kg/Month

Product Description

Product pictures



Introduction:

it is a kind of hardfacing electrode for titanium calcium type,and with CoCrMo casting alloy core,

coating by dipping into the legal system,suitable for DC reverse

Application:

Used for surfacing welding on occasions requiring excellent wear-resistance, corrosion-resistance

enough under 650ºC,such as the surfacing welding of high temperature and pressure valves,hot

shearing knives etc.Also used for surfacing welding on workpieces under the conditions withstood

impact and alternated cooling and heating.

Chemical Composition of Deposited Metal (%)

 

Chemical Composition	C	Cr	Mn	Si	W
Requirement	1.00~1.70	26.00~32.00	≤2.00	≤2.00	7.00~10.00

 

Deposited Metal Hardness: HRC≥40 

Diameters/Reference Current (DC+)

 

Electrode Diameter (mm)	3.2	4.0	5.0
Welding Current (A)	120-160	140-190	150-210

 

Notes on Usages:

1.The electrodes must be baked under 200ºC for an hour before welding.

2.As far as possible with short arc welding, and welding work to maintain the vertical.

3.According to the size of the work and the type of the base material should be 300~600ºC preheating.

4.After the welding, it should be in 600 ~ 700ºC tempering after 1 hour in slowly cooled or will work

immediately placed in dry and hot sandbox or Barilla slow cooling, to avoid cracks.

5.The surfacing layer must be rough grinding, if found defects, according to the above steps to weld

repair and slow cooling.

Packages:
 

Size: 2.7mm*1000mm

package: 5 kg/inner box

Size: 3.2mm*1000mm

package: 5 kg/inner box

Size: 4.0mm*1000mm

package: 5 kg/inner box

outer box is cardboard carton

However, we can do it as client's request: 

Delivery:7-15 days after order confirmed

               If you need more information on our products details ,please feel free to contact us !